Tungsten Carbide Cemented Carbide Polished Grinding Round Bar Rod for Engraving Tools

• Type: Drawing Die Parts
• Material: Wcco
• Application: Electronic, Hardware, Machinery, Daily Use, Furniture, Household Applicances, Car
• Certification: GS, RoHS, CE, ISO9001
• Hardness: 91.8hra
• Strength: 3800MPa
• Model NO.: dia. 5*100mm 45degree
• Unground: Grinding H6, H7, H6.H7 Ect
• Surface: Polished
• Co Content: 10%
• Wc Content: 90%
• Transport Package: 25kg. Carton
• Specification: YL10.2
• Trademark: ZZUP
• Origin: Zhuzhou, Hunan, China
• HS Code: 820900100
• Production Capacity: 10000000PCS/Month

Product Description

1. Grade: YL10.2,YG10X,YG12X,YG15,YG20,YG10,YG8,YG8 etc.
2. diameter from 0.3mm~100mm,
3. length from 10mm~1000mm
4. tolerance for diameter (.-0.05~+0.05),tolerance for length (0~+0.2mm).
5. angles of tips are 30º,60º,90º

Material	tungsten carbide
Color	grey
Standard	DIN GB ISO JIS BA ANSI
Grade	YL10.2,YG10X,YG12X,YG15,YG20,YG10,YG8,YG8 etc
Brade	ZZUP
Grain size	0.6um
Used	for milling 45HRC,50HRC,60HRA metals

Grade	YL10.2
Contens	10%co 90%wc
Grain Size	0.7um
Density	14.45g/cm3
Hardness	91.8HRA
TRS	3800MPa
Out Diameter	5mm
Length	100mm
Degree	45°

Grade	Density (g/cm3)	Hardness (HRA)	T.R.S (MPa)	Grain size (μm)	Composition (%)	Equal to ISO
YL10.2	14.4~14.6	≥92.2	≥4000	0.6~0.8	10% CO 90% WC	K30
YG6X	14.85~15.0	≥92.0	≥1860	0.8~1.0	6% CO 94%  WC	K10
YG15	14.0~14.1	≥85.0	≥2800	1.2~2.0	15%Co 85% WC	/
YG10	14.5~14.6	≥85.5	≥2600	1.2~2.0	10%Co 90% WC	K20
YG8	14.65~14.85	≥89.5	≥2320	1.2~2.0	8% CO 92%WC	K20
YG6	14.85~15.05	≥90.0	≥2150	1.2~2.0	6% CO 94%WC	K10