| Classification: | Heavy Metal |
|---|---|
| Co: | 12% |
| Wc: | 88% |
| Hardness: | 88.5hra |
| Density: | 14.6g/cm3 |
| T.R.S: | 2680MPa |
| Samples: |
|---|
| Customization: |
|---|
Suppliers with verified business licenses
Audited Supplier 
|
Grade
|
Density g/cm3
|
Hardnes HRA
|
T.R.S Mpa
|
Performance&application recommended
|
|
YG6
|
14.90
|
90.5
|
2400
|
Good wear resistance,suitable for machining hard, rawwood,aluminum section bar,brass rod and cast iron.
|
|
YG6X
|
14.85
|
92.5
|
2000
|
Wear resistance higher than YG6,suitable for machining hard,rawwood,aluminum section bar,brass rod and cast iron.
|
|
YG8
|
14.7
|
89.8
|
2800
|
High wear and impact resistance,suitable for machining dry wood,soft wood and non-ferrous metal section bar
|
|
YS2T
|
14.25
|
92.0
|
2400
|
Fine grain alloy,with high wear resistance,bending strength,bonding resistance and thermal strength.lt is suitable formachining refractory alloys,stainless steel,high manganesesteel,etc.
|
|
YL10.2
|
14.45
|
91.8
|
3000
|
Wear resistance and strength comparatively higher,suitable for machining cast iron,non-ferrous metal and non-metallid materials
|
|
W(mm)
|
T(mm)
|
L(mm)
|
|
W(mm)
|
T(mm)
|
L(mm)
|
|
3~10
|
1.2~10
|
10~800
|
|
50~60
|
1.2~10
|
10~800
|
|
10~20
|
1.2~10
|
10~800
|
|
60~70
|
1.2~10
|
10~800
|
|
20~30
|
1.2~10
|
10~800
|
|
70~80
|
1.2~10
|
10~800
|
|
40~50
|
1.2~10
|
10~800
|
|
80~100
|
1.2~10
|
10~800
|
|
17
|
1.2~10
|
10~800
|
|
|
|
|
Suppliers with verified business licenses
Audited Supplier 
){kind=link}
){kind=link}