The Tungsten Carbide Bars, Blanks are made by Extrusion from the highest purity of Materials and Sinter Hiped. Be of very high quality and tool peroformances, the grade for Cutting tools are usually in Sub-micron Grain and Ultra-fine Grain. As demand,the other grade can be custom-made.tungsten carbide round rod is mainly applied in making drills, end mills and reamers. And it is also used for cutting, punching and measuring tools. It is used in the industries of paper making, package, printing, non-ferrous metal processing.
Customization Support
| Grade | YL10.2 |
| W(mm) | 12 |
| L(mm) | 100 |
| T(mm) | 4 |
| Hardness | 14.45 |
| Density g/cm3 | 91.8 |
| T.R.S Mpa | 3000 |
|
W(mm)
|
T(mm)
|
L(mm)
|
|
W(mm)
|
T(mm)
|
L(mm)
|
|
3~10
|
1.2~10
|
10~800
|
|
50~60
|
1.2~10
|
10~800
|
|
10~20
|
1.2~10
|
10~800
|
|
60~70
|
1.2~10
|
10~800
|
|
20~30
|
1.2~10
|
10~800
|
|
70~80
|
1.2~10
|
10~800
|
|
40~50
|
1.2~10
|
10~800
|
|
80~100
|
1.2~10
|
10~800
|
|
17
|
1.2~10
|
10~800
|
|
|
|
|
|
Grade
|
Density g/cm3
|
Hardnes HRA
|
T.R.S Mpa
|
Performance&application recommended
|
|
YG6
|
14.90
|
90.5
|
2400
|
Good wear resistance,suitable for machining hard, rawwood,aluminum section bar,brass rod and cast iron.
|
|
YG6X
|
14.85
|
92.5
|
2000
|
Wear resistance higher than YG6,suitable for machining hard,rawwood,aluminum section bar,brass rod and cast iron.
|
|
YG8
|
14.7
|
89.8
|
2800
|
High wear and impact resistance,suitable for machining dry wood,soft wood and non-ferrous metal section bar
|
|
YS2T
|
14.25
|
92.0
|
2400
|
Fine grain alloy,with high wear resistance,bending strength,bonding resistance and thermal strength.lt is suitable formachining refractory alloys,stainless steel,high manganesesteel,etc.
|
|
YL10.2
|
14.45
|
91.8
|
3000
|
Wear resistance and strength comparatively higher,suitable for machining cast iron,non-ferrous metal and non-metallid materials
|