1.5*6*330mm Yl10.2 Cemented Carbide Blades and Flat Bars with High Hardness & Toughness Fine Grinding

• Classification: Heavy Metal
• Co: 10.2%
• Wc: 89.8%
• Hardness: 90.5hra
• Density: 14.5g/cm3
• T.R.S: 2500MPa
• Surface: Only Sintered
• Width: 6mm
• Thickness: 1.5mm
• Length: 330mm
• Transport Package: 25kg. Carton
• Specification: YL10.2
• Trademark: ZZUP
• Origin: Zhuzhou, Hunan, China
• HS Code: 820900100
• Production Capacity: 10000000PCS/Month

Product Description

1.5*6*330mm YL10.2  cemented carbide blades and flat bars with High hardness & toughness fine grinding 


Specifications
1. YG8,YG6,YG10,YG15,YG20,YG25,YL10.2,YS2T,YG6X etc all kinds of grade
s for your choose.
2. Supply sintered or ground and polished surface.
3. Can HIP sintered,higher harndess, strength and density.
4. We have more than 1000 sets molds for different sizes.
5. Supply customized package.
6. Can product customize sizes and shape.

 

Products Show

 

Grades choosing

Grade	Density g/cm3	Hardnes HRA	T.R.S Mpa	Performance&application recommended
YG6	14.90	90.5	2400	Good wear resistance,suitable for machining hard, rawwood,aluminum section bar,brass rod and cast iron.
YG6X	14.85	92.5	2000	Wear resistance higher than YG6,suitable for machining hard,rawwood,aluminum section bar,brass rod and cast iron.
YG8	14.7	89.8	2800	High wear and impact resistance,suitable for machining dry wood,soft wood and non-ferrous metal section bar
YS2T	14.25	92.0	2400	Fine grain alloy,with high wear resistance,bending strength,bonding resistance and thermal strength.lt is suitable formachining refractory alloys,stainless steel,high manganesesteel,etc.
YL10.2	14.45	91.8	3000	Wear resistance and strength comparatively higher,suitable for machining cast iron,non-ferrous metal and non-metallid materials

Other grades and sizes can be offered as per customers' requirements




Sizes choosing

W(mm)	T(mm)	L(mm)		W(mm)	T(mm)	L(mm)
3~10	1.2~10	10~800		50~60	1.2~10	10~800
10~20	1.2~10	10~800		60~70	1.2~10	10~800
20~30	1.2~10	10~800		70~80	1.2~10	10~800
40~50	1.2~10	10~800		80~100	1.2~10	10~800
17	1.2~10	10~800

 

 

Packing details






Shipping ways








Production process

Introduction to cemented carbide:

Cemented carbide are powder metallurgy products mainly composed of hard phase and bonded phase. The hard phase is hard and consists mainly of various carbides. The main carbides are tungsten carbide (WC), titanium carbide (TiC), tantalum carbide (TaC) and niobium carbide (NbC). In most cases, cobalt is used as a bonding phase. In cemented carbide factories, cemented carbide is mixed, pressed and sintered.

Cemented carbide is often used in lathe tools, impact drill bits, glass cutter heads, ceramic tile cutters, hard and not afraid of annealing, but brittle quality. Belongs to the rare metal, with high hardness, wear resistance, strength and toughness is good, heat resistance, corrosion resistance and a series of excellent properties, especially its high hardness and wear resistance, even at 500ºC is basically unchanged, still has a high hardness at 1000ºC. Cemented carbide is widely used as tool materials, such as turning tool, milling cutter, planer, drill, boring cutter, etc., for cutting cast iron, non-ferrous metals, plastics, chemical fiber, graphite, glass, stone and ordinary steel, but also can be used to cut heat-resistant steel, stainless steel, high manganese steel, tool steel and other difficult to process materials. The cutting speed of new carbide tools is now hundreds of times that of carbon steel.

Cemented carbide can also be used to make drilling tools, mining tools, drilling tools, measuring tools, wear-resistant parts, metal abrasives, cylinder linings, precision bearings, nozzles, etc.