20%Co Od135*ID78*40mm Tungsten Carbide Roller Die Cassette, Carbide Wire Guide Jaw for Wire Straightener

• Customization: Available
• Structure: Single End
• Pressure: High Pressure Mechanical Seals
• Model NO.: OD135*ID78*40mm
• Speed: High-Speed Mechanical Seal
• Temperature: High Temperature Mechanical Seal
• Performance: Wear
• Standard: Standard, Nonstandard
• Type: HU7
• Balance: Balanced
• Grade: Yg15
• Usage: as Milling Roller
• Surface: Grinding and Polished
• Transport Package: 25kg. Carton
• Specification: OD135*ID78*40mm
• Trademark: ZZUP
• Origin: Zhuzhou, Hunan, China
• HS Code: 820900100
• Production Capacity: 10000000PCS/Month

Product Description

  Tungsten carbide wire guide rollers are made from original tungsten carbide material,due to its high wear resistance,transeverse rupture strength and 10-15 times service life than steel rollers,it is widly used in steel works for the mechanical descaling,straightenning and plattenning for entry wires and rod in reduction mills and improving the mechanical property of the cold rolled wire.

  Tungsten carbide wire guiding rolls could be divided into V type,R type and U type according to the shape of the roller groove.tungsten carbide V type roller mainly are 90°,110°,120°,etc.tungsten carbide R type could R2.0mm to R25.0mm,the outer diameter are available from Φ1.0-Φ500.0mm.

grade	YG15
content	15%co 85%wc
density	14.0g/cm3
hardness	87.0hra
TRS	3000MPa
sizes	OD135*ID78*40mm

Grade	Density g/cm3	Hardnes HRA	T.R.S Mpa	Performance&application recommended
YG6A	14.85	92.5	2000	Fine grain alloy,good wear resistance.it is suitable for manufacturing forming cutter,wear-resistant parts etc.
YG8	14.7	89.8	2800	High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YG11	14.4	88.5	2900	High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YG15	14.0	87.0	3000	Suitable for manufacturing punching dies, wear-resistant parts.
YG20	13.5	85.5	2800	High bending strength,suitable for manufacturing progressive dies and other punching dies.
YG25	13.1	81.5	2950	High bending strength,wear resistance lower than YM6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YS2T	14.25	92.0	2500	Fine grain alloy, with high wear resistance, bending strength, bonding resistance and thermal strength. it is suitable for machining refractory alloys,stainless steel, high manganese steel, etc.