100% Raw Material Yn6 Tungsten Carbide Mold Hard Alloy Wear Non-Magnetic Rings

• Customization: Available
• Structure: Single End
• Pressure: High Pressure Mechanical Seals
• Model NO.: od55xid16x3mm
• Speed: High-Speed Mechanical Seal
• Temperature: High Temperature Mechanical Seal
• Performance: Wear
• Standard: Standard, Nonstandard
• Type: HU7
• Balance: Balanced
• Grade: Yn6
• Contents: 6%Co,92%Wc,2%Ni
• Density: 14.0g/cm3
• Hardness: 90hra
• Trs: 1400MPa
• Surface: Blank
• Transport Package: 25kg. Carton
• Specification: od55xid16x3mm
• Trademark: ZZUP
• Origin: Zhuzhou, Hunan, China
• HS Code: 820900100
• Production Capacity: 10000000PCS/Month

Product Description

     Cemented carbide is an alloy material made of hard compounds of refractory metals and bonding metals through powder metallurgy.
Cemented carbide has a series of excellent properties such as high hardness, wear resistance, good strength and toughness, heat resistance, and corrosion resistance. In particular, its high hardness and wear resistance remain basically unchanged even at a temperature of 500°C, and it still has a high hardness at 1000°C.
Cemented carbide is widely used as a tool material, such as turning tools, milling cutters, planers, drills, boring tools, etc., for cutting cast iron, non-ferrous metals, plastics, chemical fibers, graphite, glass, stone and ordinary steel. It can also be used to cut difficult-to-process materials such as heat-resistant steel, stainless steel, high manganese steel, and tool steel.

grade	YG6
content	6%CO 92%WC 2%Ni
density	14.0g/cm3
hardness	90.0hra
TRS	1400MPa
sizes	55*16*3mm

 

Grade	Density g/cm3	Hardnes HRA	T.R.S Mpa	Performance&application recommended
YG6A	14.85	92.5	2000	Fine grain alloy,good wear resistance.it is suitable for manufacturing forming cutter,wear-resistant parts etc.
YG8	14.7	89.8	2800	High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YG11	14.4	88.5	2900	High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YG15	14.0	87.0	3000	Suitable for manufacturing punching dies, wear-resistant parts.
YG20	13.5	85.5	2800	High bending strength,suitable for manufacturing progressive dies and other punching dies.
YG25	13.1	81.5	2950	High bending strength,wear resistance lower than YM6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YS2T	14.25	92.0	2500	Fine grain alloy, with high wear resistance, bending strength, bonding resistance and thermal strength. it is suitable for machining refractory alloys,stainless steel, high manganese steel, etc.