Match 5mm and 10mm Diameter Carbide Ball 50ml Tungsten Carbide Mill Jar

• Customization: Available
• After-sales Service: Vpii
• Warranty: Vpii
• Model NO.: carbide mill jar
• Condition: New
• Certification: CE, RoHS, GS, ISO9001
• Standard: DIN, ASTM, GOST, GB, JIS, ANSI
• Customized: Customized
• Material: Alloy
• Application: Metal Recycling Machine, Metal Cutting Machine, Metal Straightening Machinery, Metal Spinning Machinery, Metal Processing Machinery Parts, Metal forging Machinery, Metal Engraving Machinery, Metal Drawing Machinery, Metal Coating Machinery, Metal Casting Machinery
• Grade: Yg8
• Hardness: 89hra
• Density: 14.8g/cm3
• T.R.S: 1850MPa
• Usage: as Milling Jar
• Surface: Grinding and Polished
• Transport Package: 25kg. Carton
• Specification: Yg8 Od64*ID50*56 mm
• Trademark: ZZUP
• Origin: Zhuzhou, Hunan, China
• HS Code: 8209009000
• Production Capacity: 10000000PCS/Month

Product Description

Match 5mm and 10mm Diameter Carbide Ball 50ml Tungsten Carbide Mill Jar
 

Products description

1. Jar Volume: 25ML~1000ML (25ML/30ML/35ML/40ML/50ML/60ML/70ML/80ML/90ML/100ML etc)
2. Match tungsten carbide or ceramics grinding ball 
3. Max Loading Capacity:2/3 capacity of the grinding jar
4. Density: 14.0g/cm³ ,14.5g/cm³, 14.8g/cm³
5. Main Chemical Compositions: WC (94%,92%,85%),Cobalt (6%,8%, 15%)
6. Surface Treatment: blank or finish
7. Abrasion Resistance: very good
8. Attachment:lid and rubber sealing gasket
9. Grinding Balls: mixed tungsten carbide ball(should be ordered separately)
10.Hardness: 85.5HRA , 89.5HRA ,90.5HRA, 91.8HRA OR 92.1HRA
11. Also product the goods according the Customize drawing 

cemented carbide  mill jar

Specifications

1. Grade: YG8 , 8% Co
2. YG8,YG6,YG3,YG10,YG15,YT14,YT5,YT05,YT15,YG20,YG25,YL10.2,YS2T,YG6X etc all kinds of grades for your choose.
3. Can product customize drawing,sizes and shape.

Products Show

 

Grades choosing
Common grades for all kinds metal

Grade	Density g/cm3	Hardnes HRA	T.R.S Mpa	Performance&application recommended
YG6A	14.85	92.5	2000	Fine grain alloy,good wear resistance.it is suitable for manufacturing forming cutter,wear-resistant parts etc.
YG8	14.7	89.8	2800	High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YG11	14.4	88.5	2900	High bending strength,wear resistance lower than YG6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YG15	14.0	87.0	3000	Suitable for manufacturing punching dies, wear-resistant parts.
YG20	13.5	85.5	2800	High bending strength,suitable for manufacturing progressive dies and other punching dies.
YG25	13.1	81.5	2950	High bending strength,wear resistance lower than YM6A, suitable for manufacturing cutter ,wear-resistant parts etc.
YS2T	14.25	92.0	2500	Fine grain alloy, with high wear resistance, bending strength, bonding resistance and thermal strength. it is suitable for machining refractory alloys,stainless steel, high manganese steel, etc.

 

Other grades and sizes can be offered as per customers' requirements