89.8hra 8% Co 25*6*13.3mm Brazing Cutting Insert Tungsten Carbide Blank Tips

• After-sales Service: Supply
• Warranty: 3 Month
• Condition: New
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: 25*6*13.3mm
• Certification: ISO9001
• Standard: DIN
• Customized: Non-Customized
• Material: Tungsten Carbide
• Application: Metal Recycling Machine, Metal Cutting Machine, Metal Straightening Machinery, Metal Spinning Machinery, Metal Processing Machinery Parts, Metal forging Machinery, Metal Engraving Machinery, Metal Drawing Machinery, Metal Coating Machinery, Metal Casting Machinery
• Hardness: 92.5hra
• Density: 14.92g/cm3
• T.R.S: 3000MPa
• Usage: for Cut Button
• Length: 25mm
• Width: 13.3mm
• Thickness: 6.0mm
• Transport Package: 25kg. Carton
• Specification: 25*6*13.3mm
• Trademark: ZZUP
• Origin: Zhuzhou, Hunan, China
• HS Code: 820900100
• Production Capacity: 100000kg/Month
• Package Size: 25.00cm * 18.00cm * 20.00cm
• Package Gross Weight: 7.000kg

Product Description

1. Grade: YG8 8% Co,92% WC , Density 14.7g/cm3,

2.sizes:25*6*13.3mm

3. YG8,YG6,YG3,YG10,YG15,YT14,YT05,YT15,YG20,YG25,YL10.2,YS2T,YG6X etc all kinds of grades for your choose.

4. Can product customize drawing,sizes and shape.

5. producting within 12 days after payment.

 Customization Support!

Grade	YG8
Contents	K20
Hardness	89.8HRA
T.R.S	2800MPa
Length	25mm
Width	13.3mm
Height	6.0mm

 

 

 

 

Grade	Density g/cm³	Hardnes   HRA	T.R.S MPα	Performance & application recommended					ISO
YG3A	15.1	94.0	1700	Suitable for finishing of cast iron and nionferrous metal.					K01~K05
YG3X	15.2	92.0	1800
YG6A	14.9	92.5	2200	Suitable for the semi-finishing cast iron and nonferrous metals and also for the machining of manganese steel and hardened steel.					K10
YG6X	14.9	91.5	2300
YG6	15.0	90.5	2400	Suitable for the roughing of cast iron and light alloys and also for      the milling of cast iron and low-alloy steel.					K15
YG8	14.7	89.8	2800						K20
YW1	13.1	91.6	1600	Suitable for finishing and semi-finishing of stainless steel and conwentional alloy steel.					M10
YW2	13.0	90.6	1800	The grade can be used for the semi-finishing of stainless stell and  low-alloy steel and it is mainly used for the machining of railway  wheel hubs.					M20
YT15	11.4	91.5	1600	Suitable for the finishing and semi-finishing for steel and cast steel with a moderate feed and rather high cutting speed.					P10
YT14	11.6	90.8	1700	Suitable for the finishing anf semi-finidhing of steel and cast steel.					P20
YT5	12.9	90.5	2200	Suitable for the heavy cutting of steel and cast steel with a  big feed rate at a medium and low speed under unfavorable working conditions.					P30