| Customization: | Available |
|---|---|
| Material: | Tungsten Carbide |
| Pressure: | High Pressure |
|
Still deciding? Get samples of US$ 3.6/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Tungsten carbide valve seat are specifically developed to resist wear at high temperatures for wellhead control valve ball. The material is based on wear-resistant carbides that are thermally stable at exhaust valve seat operating temperature. These kind valve parts can be used in float control pumps for oil and gas and some other hostile enviroment.Mediums include gas,water,oil,sand,wax,asphalt and etc.
|
Grade
|
Density
(g/cm3)
|
Hardness
(HRA)
|
T.R.S
(MPa)
|
Grain size
(μm) |
Compositions
(%)
|
Specifications |
|
YG10X
|
14.6
|
91.8
|
3000
|
0.6~0.8
|
10% CO 90% WC
|
With high hardness,wear resistance,corrosion resistance,anti bending.tungsten carbide ball is used to replace steel
ball,especially YN6,containing Ni 2%,corrosion resistance is more excellent.
|
|
YG6X
|
14.85
|
92.0
|
1860
|
0.8~1.0
|
6% CO 94% WC
|
|
|
YG8
|
14.80
|
89.5
|
2320
|
1.2~2.0
|
8% CO 92% WC
|
|
|
YG6
|
14.85
|
90.0
|
2150
|
1.2~2.0
|
6% CO 94% WC
|
|
|
YN6
|
14.0
|
90.0
|
1400
|
1.2~2.0
|
6% CO 92% WC 2% Ni
|
|
common sintered balls diameters (mm)
|
|||||||
|
0.4
|
0.5
|
0.8
|
1.0
|
2.0
|
3.0
|
4.0
|
5.0
|
|
6.0
|
7.0
|
8.0
|
9.0
|
10.0
|
11.0
|
12.0
|
13.0
|
|
14.0
|
15.0
|
16.0
|
17.0
|
18.0
|
19.0
|
20.0
|
21.0
|
|
22.0
|
23.0
|
24.0
|
25.0
|
26.0
|
27.0
|
28.0
|
29.0
|
|
30.0
|
31.0
|
32.0
|
35.0
|
36.0
|
37.0
|
38.0
|
39.0
|
|
40.0
|
41.0
|
42.826
|
45.0
|
50.0
|
52.0
|
55.0
|
60.0
|
|
62.0
|
65.0
|
70.0
|
75.0
|
80.0
|
90.0
|
|
|
|
we have more than 100 kinds of diameter for your choose,other diameters pls chat with sellers.
|
|||||||
){kind=link}