Good Performance Yg8 Tungsten Carbide Bar for Machining Dry Wood

• Application: Industrial
• Standard: AISI
• Alloy: Alloy
• Shape: Square
• Type: Tungsten Bars
• Density: 14.7g/cm3
• Model NO.: YG8
• Hardness: 89.8hra
• T.R.S: 2800MPa
• Grade: Yg8
• Advantage: High Wear and Impact Resistant
• Usage: Pungching Dies
• Package: Standard Export Package
• Material: Tungsten Carbide,Heavy Alloy,Pure
• Surface: Ground
• Transport Package: Carton
• Specification: YG8
• Trademark: ZZUP
• Origin: Zhuzhou, Hunan, China
• HS Code: 8209009000
• Production Capacity: 10000000PCS/Month

Product Description

Overpressure sintering tungsten carbide plates have excellent red toughness,high hardness,good wear resistance,high elasticmodulus,high strength,good chemical stability,acid,alkali,high temperature oxidation,Low impact toughness,low expansion coefficient,thermal conductivity,the characteristics of the conductive similar to iron and other alloy.

1.   having all kind sizes for your choose,can suply less than 400mm length.

2.   Sintere by vacuum sintering furnace and HIP machine with excellent specifications without any hole.

3.   suply blank plate with tolerance(-0.15~+0.15)or (0~+0.3).

4.   can grinding and polishing the side and blading.

5.   delivery time is 12 days.
 

Customization Support

Grades	YG8
Density(g/cm3)	14.7
Hardness(HRA)	≥89.5
T.R.S(Mpa)	≥2800
Parameter(mm)	3.3mm*10mm*330mm
Length(mm)	330mm
Type	H6 Grinding

 

grade	Density (g/cm³)	T.R.S(Mpa)	Hardness    HRA	performance& application recommended	Equivalent to ISO
YG6	14.8	2150	90.0	High wear resistance,used for processing hard wood,original wood,aluminum section bar,brass rod and cast iron.	K20
YG6A	14.9	1860	92.0	Better wear resistant than YG6,used for processing hard wood,original wood,aluminum section bar,brass rod and cast iron.	K10
YG8	14.8	2320	89.5	Wear and perussion resistance,used for processing hard wood,soft wood,ferrous and non-ferrous	K30
YS2T	14.6	2350	92.0	Fine grain carbide with high wear resistance,high bending strength ,high resistance to bonding and high thermal strenght.apply to machining refractory alloys/stainless steel and high manganness steel ect.	M10
YS25	13.8	2200	91.0	Carbide grade with high hardness and good wear-resistance,suitable for rough turning,milling and planing of carbide steel,cast steel,high intensity steel and steel alloy	P25
YL10.2	14.5	2150	92.2	Wear resistance and strength comparatively higher,suitable for processing castiron,non-ferrous,and non-metal materials	/

a