| Customization: | Available |
|---|---|
| Hardness: | 91.8hra |
| Grade: | Yl10.2 |
|
Still deciding? Get samples of US$ 5.5/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Tungsten carbide thimble is made of high-quality tungsten carbide material by precision equipment grinding, polishing made of thimble, commonly known as: thimble, support needle, double thimble, flat thimble, insert needle, PIN needle. Because it uses high-quality tungsten carbide material with high hardness 92.0hRA and 4000MPa bending strength, it has high wear resistance and excellent corrosion resistance. It is usually used in plastic moulds. It plays a role in separating plastic products from the moulds, and can also be used through thin and long pinholes. It is often used for lathes and grinding machines to support the workpiece and make the workpiece revolve around it. It is also suitable for making tungsten carbide electrode rod in photoelectric industry. The tip Angle is controlled between 10° and 15°. It is mainly used for automatic solid crystal machine equipment, supporting (top up) auxiliary vacuum adsorption system.
|
Material
|
tungsten carbide
|
|
Color
|
grey
|
|
Standard
|
DIN GB ISO JIS BA ANSI
|
|
Grade
|
YL10.2,YG10X,YG12X,YG15,YG20,YG10,YG8,YG8 etc
|
|
Brade
|
ZZUP
|
|
Grain size
|
0.6um
|
|
Used
|
for milling 45HRC,50HRC,60HRA metals
|
|
Grade
|
Density g/cm3
|
Hardnes HRA
|
T.R.S Mpa
|
Performance&application recommended
|
|
YG6
|
14.90
|
90.5
|
2400
|
Good wear resistance,suitable for machining hard, rawwood,aluminum section bar,brass rod and cast iron.
|
|
YG6X
|
14.85
|
92.5
|
2000
|
Wear resistance higher than YG6,suitable for machining hard,rawwood,aluminum section bar,brass rod and cast iron.
|
|
YG8
|
14.7
|
89.8
|
2800
|
High wear and impact resistance,suitable for machining dry wood,soft wood and non-ferrous metal section bar
|
|
YS2T
|
14.25
|
92.0
|
2400
|
Fine grain alloy,with high wear resistance,bending strength,bonding resistance and thermal strength.lt is suitable formachining refractory alloys,stainless steel,high manganesesteel,etc.
|
|
YL10.2
|
14.45
|
91.8
|
3000
|
Wear resistance and strength comparatively higher,suitable for machining cast iron,non-ferrous metal and non-metallid materials
|