Fine Grinding Polished Carbide Section Differential Punching Needle Rod

• Product Type: Rod
• Material: Wcco
• Carbon Content: Medium Carbon
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• PCD: 100mm
• ET: 15mm
• Hole: 1.0
• Co: 10%
• Wc: 90%
• Hardness: 91.8hra
• Strength: 3500MPa
• Outdiameter: 10mm
• Length: 110(0~+0.5)
• Grinding Request: Grinding H6, H7, H6.H7 Ect
• Transport Package: 25kg. Carton
• Specification: YL10.2
• Trademark: ZZUP
• Origin: Zhuzhou, Hunan, China
• HS Code: 820900100
• Production Capacity: 10000000PCS/Month

Product Description

Products description

1. Grade: YL10.2,YG10X,YG12X,YG15,YG20,YG10,YG8,YG8 etc.
2. diameter from 0.3mm~100mm,
3. length from 10mm~1000mm
4. tolerance for diameter (.-0.05~+0.05),tolerance for length (0~+0.2mm).
5. also can make angles of tips are 30º,60º,90º

Product Name	Dia 3*L 100mm h6 poslihed grinding tungsten carbide punching needle rod
Material	tungsten carbide
Color	grey
Standard	DIN GB ISO JIS BA ANSI
Grade	YL10.2,YG10X,YG12X,YG15,YG20,YG10,YG8,YG8 etc
Brade	ZZUP
Grain size	0.6um
Used	for milling 45HRC,50HRC,60HRA metals

 

Products Show

 

Grade specification
 

Grade	Density(g/cm3)	Hardness (HRA)	T.R.S (MPa)	Grain size       (μm)	Composition          (%)	Equal to ISO
YU12	14.1~14.15	.≥92.5	≥4000	0.2~0.5	12% CO 88% WC	K40~K50
YL10.2	14.4~14.6	≥92.2	≥4000	0.6~0.8	10% CO 90% WC	K20~K30
YG6X	14.85~15.0	≥92.0	≥3860	0.8~1.0	6% CO 94%  WC	K05
YG15	14.0~14.1	≥85.0	≥2800	1.2~2.0	15%Co 85% WC	K30~K40
YG10	14.5~14.6	≥85.5	≥2600	1.2~2.0	10%Co 90% WC	K20
YG8	14.65~14.85	≥89.5	≥2320	1.2~2.0	8% CO 92% WC	K20
YG6	14.85~15.05	≥90.0	≥2150	1.2~2.0	6% CO 94% WC	K10

sizes and polished details

Diameter(mm)	Length(mm)	grinding and polishing
0.3~1.0	5~330	h6,h7,H6 or H7
1.0~3.0	5~330	h6,h7,H6 or H7
4.0~80	5~1000	h6,h7,H6 or H7

Packing details





Shipping ways







Production 

Tungsten carbide thimble /needle /grinding point rod introduction:
Tungsten carbide thimble is made of high-quality tungsten carbide material by precision equipment grinding, polishing made of thimble, commonly known as: thimble, support needle, double thimble, flat thimble, insert needle, PIN needle. Because it uses high-quality tungsten carbide material with high hardness 92.0hRA and 4000MPa bending strength, it has high wear resistance and excellent corrosion resistance. It is usually used in plastic moulds. It plays a role in separating plastic products from the moulds, and can also be used through thin and long pinholes. It is often used for lathes and grinding machines to support the workpiece and make the workpiece revolve around it. It is also suitable for making tungsten carbide electrode rod in photoelectric industry. The tip Angle is controlled between 10° and 15°. It is mainly used for automatic solid crystal machine equipment, supporting (top up) auxiliary vacuum adsorption system.
Tungsten steel thimble production process:
Ingredients (according to the requirements of applicable selection of tungsten carbide powder + cobalt powder) to the mix - crushing - drying, sieving after forming agent and dry again to sieving mixture system, the mixed system, pressing - molding - Germany import vacuum suit low sintering sintering furnace - after sintered blank - test (nondestructive ultrasonic flaw detection) - blank dimensions accuracy test - cutting molding to coarse grinding, fine grinding Polishing → inspection → packaging → storage.
Characteristics of tungsten steel thimble:
1.Due to the addition of tantalum carbide TaC with excellent wear resistance and TiC with excellent heat and wear resistance in the alloy composition, it has high wear resistance and its service life is more than 3 times that of SKH51 high speed steel and 65Mn manganese steel.
2.Precise size, high machining accuracy, polishing finish Ra≥0.012 mirror effect.
3.Tungsten carbide thimble has excellent corrosion resistance without rust, can work in acid and alkaline environment, can greatly reduce maintenance cost and maintenance time.