High Density 14.85g/cm3 Wear Resistant Tungsten Carbide Yg6X 12*18*150mm for Cutting Brass Rods

• After-sales Service: Vpii
• Warranty: Vpii
• Condition: New
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: 12*18*150mm
• Certification: ISO9001
• Customized: Customized
• Material: Alloy
• Application: Metal Cutting Machine, Metal Processing Machinery Parts
• Hardness: 92.5hra
• Trs: 2000MPa
• Density: 14.85g/cm3
• Parameter: Yg6X 12*18*150mm
• Usage: Machining Tools Part
• Cobalt Content: 15%
• Grade: K10
• Transport Package: 25kg. Carton
• Specification: 12*18*150mm
• Trademark: ZZUP
• Origin: Zhuzhou, Hunan, China
• HS Code: 8209009000
• Production Capacity: 10000000PCS/Month
• Package Size: 33.00cm * 23.00cm * 12.00cm
• Package Gross Weight: 1.500kg

Product Description

Overpressure sintering tungsten carbide plates have excellent red toughness,high hardness,good wear resistance,high elasticmodulus,high strength,good chemical stability,acid,alkali,high temperature oxidation,Low impact toughness,low expansion coefficient,thermal conductivity,the characteristics of the conductive similar to iron and other alloy.

1.   having all kind sizes for your choose,can suply less than 400mm length.

2.   Sintere by vacuum sintering furnace and HIP machine with excellent specifications without any hole.

3.   suply blank plate with tolerance(-0.15~+0.15)or (0~+0.3).

4.   can grinding and polishing the side and blading.

5.   delivery time is 12 days.
 

Customization Support

Grades	Yg6X
Density(g/cm3)	14.85
Hardness(HRA)	≥92.5
T.R.S(Mpa)	≥2000
Parameter(mm)	12mm*18mm*150mm
Length(mm)	150
Type	H6 Grinding

grade	Density (g/cm³)	T.R.S (Mpa)	Hardness HRA	performance& application recommended	Equivalent to ISO
YG6	14.9	2400	90.5	High wear resistance,used for processing hard wood,original wood,aluminum section bar,brass rod and cast iron.	K10
YG6A	14.85	2000	92.5	Better wear resistant than YG6,used for processing hard wood,original wood,aluminum section bar,brass rod and cast iron.	K10
YG8	14.7	2800	89.8	Wear and perussion resistance,used for processing hard wood,soft wood,ferrous and non-ferrous	K20
YS2T	14.25	2400	92.0	Fine grain carbide with high wear resistance,high bending strength ,high resistance to bonding and high thermal strenght.apply to machining refractory alloys/stainless steel and high manganness steel ect.	K30
YS25	13.0	2200	91.0	Carbide grade with high hardness and good wear-resistance,suitable for rough turning,milling and planing of carbide steel,cast steel,high intensity steel and steel alloy	/
YL10.2	14.45	3000	91.8	Wear resistance and strength comparatively higher,suitable for processing castiron,non-ferrous,and non-metal materials	K30